SHANGHAI HAOHAI CHEMICAL CO.,LTD In-depth analysis of the actual needs of target customers, combined with its own advantages resources, successfully developed CE Adhesive Sealant Expanding Construction PU Foam Caulk Manufacturer. It is designed to meet the industry criterion. In aspect of the product design, our design team always pays close attention to the customers' taste and industry trends. Thanks to this, our CE Adhesive Sealant Expanding Construction PU Foam Caulk Manufacturer can fully attract people's attention with its unique appearance. Moreover, it is excellent performance, making it worth the investment.
|Place of Origin:||Shanghai, China||Main Raw Material:||POLYURETHANE|
SHANGHAI HAO HAI CHEMICAL
|PU foam, PU adhesive, PU sealant, PU insulation|
|Size:||750ml / 500ml / 300ml|
|Packing:||12 or 15 cans per carton|
|Storage Life:||12 months when stored at 20°C|
Key Technical Indices:
|Behavior:||Stable foam, CFC free|
|Max. Yield rate:||60 times|
|Elongation at Break:||8 - 20%|
|Shear Strength:||22 - 50kPa|
|Compression Strength:||35 - 100kPa at 10% compression|
|Surface curing time:||≤ 15 min|
|Yield Per 100ml:||5 - 6L|
|Temperature Tolerance Range:||-40°C~+100°C|
Guide For Use:
1. It can be applied to damp surfaces.
2. OCF is moisture curing.The more moisture, the quicker the cure.
3. It must be protected from Uvin External application to prevent discoloration and deterioration of the foam.
4. Conventional paints can be applied to the foam.
5. In can be used in temperature range of 5-40°C,if in low temperature condition, we suggest that it should be
placed in 25-30°C circumstance for 30 minutes to ensure the better performance.
6. Uncured foam can be removed with solvent. But after cure, foam can only be removed mechanically.
One component foaming fill, convenience, easiness, efficiency, and reduced labor are promised in application.
High filling degree
|After polyurethane prepolymer is ejected, its volume increases rapidly, filling the hole to its extreme depth and ensuring high filling degree.|
|Good cohesive force||
Thanks to multiple carbamate radicals contained, polyurethane foam can tightly adhere to cement mortar and PVC plate, ensuring that the wind pressure to the window frame is evenly distributed among the four walls of the opening, instead of being withstood exclusively by spanker bolts on several fixed plates.
When filling and foaming, excessive foam will flow out, without causing deformation of the window frame.
|High sealing performance||
Ultimately, polyurethane foam will constitute a half rigid closed cell material that blocks air flow, insulates sound waves, and resists shock.
|Easiness in finishing||
As the foam cures, the protruding part can be cut and trimmed by a cutter easily.
As the foam cures, brushing the surface with coatings and emulsion paints can prevent aging due to exposure to ultraviolet.
|Long service life||
Properly painted open-air PU foam will not be prone to aging, giving a service life up to 50 years.
|Self-extinguishing performance||Flames on PU Foam will be automatically extinguished, showing compliance with the DIN 4102-B2 requirements.|
Curde foam can put up with temperature -30°C—— 100°C,with resistance against solvent, acid, and alkali.
|Environment-friendliness&energy conservation||CFC free foam does not harm the atmospheric ozone layer. Besides, the cured foam causes no hazards to human and the high sealing performance ensures reduced loss of energy.|
The foam has no corrosive effect on the window frame material.
Project Case - Shanghai World Expo 2010
GET IN TOUCH WITH US
In PU foam (OCF) industry, Haohai is one of the leading PU foam manufacturers in China.